摘 要：为了增加光电极光生电子传输通道并提高其光敏剂的负载能力,采用两步水热法制备了一种新颖的TiO2-ZnO纳米棒分级结构.采用水热法在FTO导电玻璃基底上生长TiO2纳米棒有序阵列膜,通过浸泡提拉在TiO2纳米棒上包覆一层ZnO溶胶,经烧结形成ZnO种子层；再次采用水热法于TiO2纳米棒上生长ZnO纳米棒,形成TiO2-ZnO纳米棒分级结构,通过旋涂辅助连续离子反应分别在TiO2纳米棒阵列和TiO2-ZnO納米棒分级结构中沉积光敏剂CdS纳米晶,形成CdS/TiO2纳米棒复合膜和CdS/TiO2-ZnO纳米分级结构复合膜.利用SEM,TEM,XRD、紫外-可见吸收光谱、瞬态光电流图谱等表征和测试手段,对样品的形貌、结构、光吸收和光电性能进行了表征和测试.结果表明,和单纯的TiO2纳米棒阵列相比,TiO2-ZnO分级结构可以沉积更多的CdS光敏剂,CdS/TiO2-ZnO纳米分级结构复合膜的光吸收性能和瞬态光电流均明显优于CdS/TiO2纳米复合薄膜.凭借优异的光电性能,TiO2-ZnO分级结构在太阳电池光阳极材料中具有很好的应用前景.
关键词：电化学；水热法；TiO2-ZnO纳米棒分级结构；CdS纳米晶；光电性能
中图分类号：O646文献标志码：A
Photoelectrochemical properties of the TiO2-ZnO nanorod
hierarchical structure prepared by hydrothermal process
SUN Bao1, ZHANG Sai2, DU Jingwen1, HAO Yanzhong1,2, PEI Juan1, LI Yingpin1
（1. School of Science, Hebei University of Science and Technology, Shijiazhuang, Hebei 050018, China； 2. School of Chemical and Pharmaceutical Engineering, Hebei University of Science and Technology, Shijiazhuang, Hebei 050018, China）
Abstract：In order to increase the transport channels of the photogenerated electrons and enhance the photosensitizer loading ability of the electrode, a new TiO2-ZnO nanorod hierarchical structure is prepared through two-step hydrothermal process. First, TiO2 nanorod array is grown on the FTO conductive glass substrate by hydrothermal proess. Then, ZnO sol is coated onto the TiO2 nanorods through dip-coating method and inverted to ZnO seed layer by sintering. Finally, the secondary ZnO nanorods are grown onto the TiO2 nanorods by the sencond hydrothermal method to form the designed TiO2-ZnO nanorod hierarchical structure. A spin-coating assisted successive ionic layer reaction method （SC-SILR） is used to deposit the CdS nanocrystals into the TiO2 nanorod array and the TiO2-ZnO nanorod hierarchical structure is used to form the CdS/TiO2 and CdS/TiO2-ZnO nanocomposite films. Different methods, such as SEM, TEM, XRD, UV-Vis and transient photocurrent, are employed to characterize and measure the morphologies, structures, light absorption and photoelectric conversion performance of all the samples, respectively. The results indicate that, compared with the pure TiO2 nanorod array, the TiO2-ZnO nanorod hierarchical structure can load more CdS photosensitizer. The light absorption properties and transient photocurrent performance of the CdS/TiO2-ZnO nanorod hierarchical structure composite film are evidently superior to that of the CdS/TiO2 nanocomposite films. The excellent photoelctrochemical performance of theTiO2-ZnO hierarchical structure reveales its application prospect in photoanode material of the solar cells.
总结:这是一篇与水热法论文范文相关的免费优秀学术论文范文资料,为你的论文写作提供参考。
参考文献：
1、 尿素均相沉淀法制备菱形Gd2O3Eu3纳米荧光粒子 摘 要： 以尿素为沉淀剂，稀土氯化物为原料，采用均相沉淀法制备Eu3+掺杂的Gd2O（CO3）2·H2O纳米粒子，经过煅烧后得到Gd2O3：Eu。
2、 Sb2S3纳米粒子敏化ZnO微纳分级结构的光电化学性能 摘要：采用电化学沉积方法，选择聚乙二醇（PEG400）和乙二胺（EDA）为添加剂，直接在ITO导电玻璃上制备了有序阵列的ZnO纳米棒，以及ZnO。
3、 光还原法制备AgBi2WO6可见光催化剂与其性能 摘要： 利用离子液体辅助醇热法制备了具有较高活性的Bi2WO6可见光催化剂，并进一步采用光还原法将Ag纳米粒子负载到Bi2WO6催化剂表面 利用。
4、 溶胶—凝胶法尺寸选择性合成ZnO纳米颗粒其光催化性能 摘要在溶胶凝胶合成过程中，分别利用超声波处理ZnO溶胶、加水至溶胶中煮沸、加庚烷至溶胶中、蒸发除去部分溶剂等简单的沉淀方法制备了10 nm以下不。
5、 法制备纳米Zr02粉体条件 摘要：采用ZrOCl2 8H20、NH3 H20为原料制备水热反应前驱物，以矿化剂（K203、KOH）溶液作为水热介质，PEG为分散剂，通过水热。
6、 静电纺丝模板法制备莫来石纤维工艺 摘 要 采用静电纺丝制备的PVP纤维为模板，以非水解溶胶-凝胶法制备的莫来石溶液为浸渍液，利用模板浸渍技术制备出莫来石纤维。研究优化铝离子浓度、。