摘 要：采用力学试验、渗水标号试验、渗水高度试验和氯离子渗透试验研究了聚丙烯（PP）单丝纤维自密实混凝土强度、抗渗性能,通过扫描电镜观察了纤维自密实混凝土的微观结构,从材料的组成结构和断裂力学原理上分析了PP单丝纤维对自密实混凝土强度以及抗渗性能的影响机理.结果表明： 当PP单丝纤维自密实混凝土体积掺量不超过0.15%时,PP纤维自密实混凝土具有较好的抗渗性能,渗水标号大于S 35；PP单丝纤维体积掺量不超过0.1%时,自密实混凝土的强度和抗水渗性能随着纤维体积掺量的增加而提高,电通量有所增加,而当体积掺量超过0.15%后,强度仍然有增长,电通量急剧增加；和普通自密实混凝土相比,0.10%单丝PP纤维自密实混凝土具有较好的强度特性和抗渗性能,28 d弯拉强度提高16.4%,28 d劈裂强度提高13.4%,56 d氯离子渗透电通量为919 C,渗水高度减少57%.
关键词：
纤维自密实混凝土；聚丙烯单丝纤维；强度；抗渗性能
中图分类号：TU528.572
文献标志码：A
文章编号：1674-4764（2013）03-0137-08
Strength Properties and Permeability of Polypropylene Monofilament
Fiber Reinforced Self-Compacting Concrete
He Xiaobing1,2,Yan Bo1
（1. College of Resources and Environmental, Chongqing University, Chongqing 400030, P.R. China；
2.State Key Laboratory Breeding Base of Mountain Bridge and Tunnel Enineering,
Chongqing Jiaotong University, Chongqing 400074, P.R.China）
Abstract：Strength properties and permeability of the self-compacting concrete, which are reinforced with polypropylene monofilament fiber of different volume fractions, were investigated through mechanical test, water permeability test and chloride permeability test （chloride penetrability based on charge passed）. Then, the microstructure of the polypropylene fiber reinforced self-compacting concrete （PFRSCC） was observed through scanning electronic microscope. The impact of polypropylene fiber on strength properties and permeability was analyzed according to the material composition and fracture theory. The results show that： 1） PFRSCC, when the volume fraction of polypropylene monofilament fiber is less than 0.15%, has good impermeability, characterized with high impermeability mark （>S 35, based on Chinese Standard Test Method T 0568-2005）； 2） When the volume fraction of polypropylene monofilament fiber is less than 0.10%, PFRSCC’s strength properties and water impermeability increase with the addition of polypropylene fiber, and electric flux increases slightly. Whilse when the volume fraction of polypropylene fiber is higher than 0.15%, electric flux increases dramatically； 3） Compared with ordinary self-compacting concrete, PFRSCC, 0.10% polypropylene fiber has 16.4% increase in flexural tensile strength, 13.4% increase in splitting strength and 57% decrease in permeation depth, and chloride ion penetrability is low, about 919 C at 56 d.
Key words：
fiber reinforced self-compacting concrete； polypropylene monofilament fiber； strength； permeability
总结:这篇密实论文范文为免费优秀学术论文范文,可用于相关写作参考。
参考文献：
1、 钻芯法检测结构混凝土强度合格性评定分析 摘 要：结构混凝土的强度极为重要，相关检测方法愈来愈多。首先介绍了几种混凝土强度的检测方法，并以钻芯法为重点，阐述了检验过程。然后分析了混凝土强。
2、 建筑混凝土抗渗性能在施工中应用 摘 要：混凝土的抗渗性，是指水泥混凝土材料抵抗压力水渗透的能力，是决定水泥混凝土耐久性最基本的因素之一。抗渗混凝土施工一般包括混凝土的配料、搅拌。
3、 浅述混凝土抗渗性能影响因素 [摘要]抗渗性是指混凝土抵抗压力水渗透的性能。影响混凝土抗渗性能的因素有很多，原材料的种类、原材料的比例、养护条件及养护方法皆能改善混凝土的抗渗。
4、 爆炸移除钢筋混凝土框架柱抗倒塌性能数值模拟 摘要：基于已有的爆炸移除钢筋混凝土框架柱的实验数据，利用有限元软件AUTODYN建立了一个分离式与整体式相结合的4层2跨钢筋混凝土框架结构的三维。
5、 回弹法检测混凝土强度应用分析 【摘要】回弹法检测混凝土强度在工程检测中的应用越来越广泛，本文在简述回弹法的原理及特点的基础上，对回弹法检测混凝土强度的实际应用进行分析，希望对。
6、 应变监测在自密实混凝土填充性能检测中应用 摘 要：采用埋设混凝土应变计检测混凝土应变来反应自密实混凝土的填充性能，通过比对试验和验证，探索采用监测混凝土应变的方式来表征自密实混凝土填充性。